Sintering, microstructure, mechanical, and antimicrobial properties of HAp‐ZnO biocomposites
Author(s) -
Saha Naresh,
Keskinbora Kahraman,
Suvaci Ender,
Basu Bikramjit
Publication year - 2010
Publication title -
journal of biomedical materials research part b: applied biomaterials
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.665
H-Index - 108
eISSN - 1552-4981
pISSN - 1552-4973
DOI - 10.1002/jbm.b.31734
Subject(s) - materials science , fracture toughness , antimicrobial , sintering , microstructure , staphylococcus epidermidis , indentation , zinc , composite material , bacteria , metallurgy , staphylococcus aureus , chemistry , organic chemistry , biology , genetics
The implant associated infection is widely considered as a major concern in the field of biomedical applications and this has been the driving force for developing HAp‐based biomaterials with antibacterial additives for possible use in prosthetic devices. In our present work, we sintered Hydroxyapatite (HAp) with different concentrations of zinc oxide microrods (ZnO) at 1250°C to produce HAp‐ZnO biocomposites. In vitro antimicrobial studies were carried out to understand how ZnO addition (up to 30 wt %) to HAp leads to the improvement in bacteria static/bactericidal property and thereby, can reduce bacterial infection on implant surface. Both Gram positive ( S. aureus , S. epidermidis ) and Gram negative bacteria ( E. coli ) were used for this study. After 4 h of incubation, it was observed that microbial activity on HAp‐20 wt % and HAp‐30 wt % ZnO are significantly reduced in comparison to control sample, independent of type of bacterial cells. Despite such improvement in antimicrobial property, an increase in ZnO addition was found to have modest influence on fracture toughness or hardness properties. A maximum up to 1.7 MPam 1/2 indentation fracture toughness and hardness of up to 6.8 GPa were measured in HAp‐ZnO biocomposites. © 2010 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 2010.