Physical characterization of different‐roughness titanium surfaces, with and without hydroxyapatite coating, and their effect on human osteoblast‐like cells
Author(s) -
Borsari Veronica,
Giavaresi Gianluca,
Fini Milena,
Torricelli Paola,
Salito Armando,
Chiesa Roberto,
Chiusoli Loris,
Volpert Andreas,
Rimondini Lia,
Giardino Roberto
Publication year - 2005
Publication title -
journal of biomedical materials research part b: applied biomaterials
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.665
H-Index - 108
eISSN - 1552-4981
pISSN - 1552-4973
DOI - 10.1002/jbm.b.30313
Subject(s) - materials science , titanium , coating , surface roughness , surface finish , titanium alloy , osteoblast , adhesion , composite material , chemical engineering , metallurgy , chemistry , in vitro , alloy , biochemistry , engineering
The aim of this study was to characterize and compare various titanium (Ti) and hydroxyapatite (HA) coatings on Ti6Al4V, in view of their application on noncemented orthopedic implants. Two innovative vacuum plasma sprayed (VPS) coatings, the first of ultrahigh rough and dense Ti (PG60, R a = 74 μm) and the second of ultrahigh rough and dense Ti coated with HA (HPG60, R a = 52 μm), have been developed, and the response of osteoblast‐like cells (MG‐63) seeded on these new coatings was evaluated in comparison to: a low roughness and sandblasted (Ti/SA, R a = 4μm) Ti6Al4V surface; Ti medium (TI01, R a = 18 μm), and high (TI60, R a = 40μm) roughness VPS coatings; and the relative Ti plus HA duplex coatings (HT01, R a = 12 μm and HT60, R a = 36 μm respectively), also obtained by VPS. PG60 coating presented no open porosity, making it dense and potentially intrinsically stronger. Cell adhesion and proliferation on PG60 was similar to those of the smoothest one (Ti/SA) and adhesion on ultrahigh roughness was lower than the medium‐ and high‐roughness coatings, whereas cell proliferation on PG60 was lower than TI60. The HA coating determined significant increases in cell proliferation at medium and high roughness levels when compared to the relative Ti coating, but not compared to the ultrahigh one; all HA‐coated surfaces showed a decrease in alkaline phosphatase activity and collagen I production. Surface morphology and the HA coating strongly affected cell behavior. However, ultrahigh values of roughness are not correctly seen by cells, and the presence of HA has no improving effects. © 2005 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 2005