Evaluation of CO 2 attack in wellbore class G cement: influence of epoxy resins, composites and minerals as additives
Author(s) -
Schütz Marta K.,
dos Santos Leonardo M.,
Coteskvisk Patrícia M.,
Menezes Sonia C.,
Einloft Sandra,
Dalla Vecchia Felipe
Publication year - 2019
Publication title -
greenhouse gases: science and technology
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.45
H-Index - 32
ISSN - 2152-3878
DOI - 10.1002/ghg.1928
Subject(s) - carbonation , epoxy , cement , chemical resistance , portland cement , materials science , compressive strength , composite material , supercritical fluid , chemistry , organic chemistry
Carbon dioxide (CO 2 ) injection into geological formations is pointed out as one of the most effective alternatives to reduce anthropogenic CO 2 emissions to the atmosphere. To promote long‐term CO 2 storage, wellbore integrity is a critical issue to be considered. Portland cement is commonly used for cementing wells, and considered chemically unstable in CO 2 ‐rich media. In this context, this study investigated the CO 2 chemical resistance of class G Portland cement modified with novel additives (epoxy resins, epoxy–clay composites, and clay minerals) at 1 and 2.5 wt% contents. Reaction times of 7 and 30 days of exposure to CO 2 in supercritical conditions were evaluated. Samples were characterized by mechanical compression tests and phenolphthalein indicator as well as field emission scanning electron microscopy in order to determine the depth of carbonation in cement. Our results indicate that although there is slight reduction in the initial compressive strength, the addition of tested additives to cement paste offers improvements in terms of chemical resistance. The optimum content of different additives was 1 wt% in order to maintain compressive strength properties and improve chemical resistance to CO 2 . The best result was achieved with an epoxy resin blend as an additive, decreasing carbonation by up to 60% (7 days of exposure to CO 2 ) and 52% (30 days of exposure to CO 2 ). Addition of montmorillonite to the epoxy blend tends to improve chemical resistance of cement paste when compared to the neat epoxy blend. © 2019 Society of Chemical Industry and John Wiley & Sons, Ltd.