Preparation of High Performance Pt/CNT Catalysts Stabilized by Ethylenediaminetetraacetic Acid Disodium Salt
Author(s) -
Liu J.M.,
Meng H.,
Li J.l.,
Liao S.j.,
Bu J.H.
Publication year - 2007
Publication title -
fuel cells
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.485
H-Index - 69
eISSN - 1615-6854
pISSN - 1615-6846
DOI - 10.1002/fuce.200700016
Subject(s) - ethylenediaminetetraacetic acid , catalysis , nanomaterial based catalyst , proton exchange membrane fuel cell , chloroplatinic acid , carbon nanotube , salt (chemistry) , methanol , nanoparticle , inorganic chemistry , chemical engineering , electrochemistry , materials science , nuclear chemistry , chemistry , chelation , nanotechnology , platinum , organic chemistry , electrode , engineering
Abstract A novel method with ethylenediaminetetraacetic acid disodium salt (EDTA‐2Na) as a stabilizing agent was developed to prepare highly dispersed Pt nanoparticles on carbon nanotubes (CNTs) to use as proton exchange membrane (PEM) fuel cell catalysts. These nanocatalysts were obtained by altering the molar ratio of ethylenediaminetetraacetic acid disodium salt to chloroplatinic acid (EDTA‐2Na/Pt) from 1:2, 1:1, 2:1 to 3:1. The well‐dispersed Pt nanoparticles of around 1.5 nm in size on CNTs were obtained when the EDTA‐2Na/Pt ratio was maintained at 1:1. And the Pt/CNT catalyst exhibited large electrochemical active surface areas, very high electrocatalytic activity and excellent stability in the oxidation of methanol at room temperature. The Pt/XC‐72R catalyst with narrow size distribution was also prepared by this method for comparison purposes. Comparison of the catalytic properties of these catalysts revealed that the activity of the Pt/CNT catalyst was a factor of ∼3 times higher than that of the Johnson Matthey catalyst and ∼2 times higher than that of our Pt/XC‐72R catalyst, which can be assigned to the high level of dispersion of Pt nanoparticles and the particular properties of the CNT supports.