Property of intrinsic flame retardant epoxy resin cured by functional magnesium organic composite salt and diethylenetriamine
Author(s) -
Gao Chengyong,
Wang Lei,
Lei Ziqiang,
Yang Li,
Xu Xiaohuan,
Guo Xing
Publication year - 2017
Publication title -
fire and materials
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.482
H-Index - 58
eISSN - 1099-1018
pISSN - 0308-0501
DOI - 10.1002/fam.2377
Subject(s) - diethylenetriamine , epoxy , fire retardant , composite number , thermogravimetric analysis , materials science , composite material , curing (chemistry) , ammonium polyphosphate , ultimate tensile strength , fourier transform infrared spectroscopy , magnesium , chemical engineering , chemistry , organic chemistry , metallurgy , engineering
Summary An efficient intrinsic flame retardants composite was prepared by curing epoxy resin with a functional magnesium organic composite salt (FMOCS, 0.685 ± 0.3 nm) and diethylenetriamine (DETA). Curing behavior, thermal and flame‐retardant properties of the cured epoxy resins were systematically investigated by infrared spectrum (FTIR), thermogravimetric analysis (TGA), vertical burning test (UL‐94) and limited oxygen index (LOI) measurement. It was found that flame retardancy and mechanical properties of the cured composite are significantly enhanced compared with DETA/EP. The LOI of the EP reached to 33%, which is much higher than the DETA/EP (19%) or its IFR composite (31%) in the optimal addition of ammonium polyphosphate (APP, 18.69 wt %), pentaerythritol (PER, 6.21 wt %) and FMOCS (3.50 wt %). Furthermore, the mechanical properties of the composite material measurement results to imply that it can enhance tensile strength (150%) and bending strength (88%) rather than DETA/EP, which were tested by impact testing machine and microcomputer control electron universal testing machines. Copyright © 2016 John Wiley & Sons, Ltd.