Poly(trimethylene terephthalate)/magnesium hydroxide composites with on‐demand thickening at high temperatures
Author(s) -
Messmore Benjamin W.,
Zudans Andrew W.,
Pottiger Michael T.,
Berl Anna G.
Publication year - 2014
Publication title -
fire and materials
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.482
H-Index - 58
eISSN - 1099-1018
pISSN - 0308-0501
DOI - 10.1002/fam.2171
Subject(s) - magnesium , rheology , materials science , composite number , viscosity , polymer , composite material , extrusion , polyester , molding (decorative) , hydroxide , chemical engineering , metallurgy , engineering
Magnesium hydroxide, when melt extruded with poly(trimethylene terephthalate) (PTT) at low concentrations (1–3 wt.%), can be melt processed during extrusion and injection molding. When the polymer is heated in the melt to 295°C, the viscosity of the composite behaves similarly to control samples and the viscosity decreases as a function of temperature. When the temperature of the composite is raised above 295°C (above the normal processing conditions for PTT), a significant change in the melt rheology of the composite is observed relative to unfilled compositions. This change in melt rheology coincides with the decomposition temperature of magnesium hydroxide and formation of magnesium oxide, a common thickening agent employed in unsaturated polyester resins. Lower processing temperature polyesters, including PTT, enable processing of the polymer in the presence of magnesium hydroxide under normal conditions. The viscosity modifier ‘turns on’ when the composite sees elevated temperature where magnesium oxide is known to form. The magnesium oxide is hypothesized to interact with PTT carboxyl end groups, providing the observed increase in viscosity. The rheological response observed in the composites is dependent on the concentration of magnesium hydroxide. During burning, the viscosity modifier results in a non‐dripping formulation of PTT. Copyright © 2012 John Wiley & Sons, Ltd.