Surface Functional Groups and Electrochemical Behavior in Dimethyl Sulfoxide‐Delaminated Ti 3 C 2 T x MXene
Author(s) -
Qian Aniu,
Seo Jung Yong,
Shi Hu,
Lee Jin Yong,
Chung ChanHwa
Publication year - 2018
Publication title -
chemsuschem
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 2.412
H-Index - 157
eISSN - 1864-564X
pISSN - 1864-5631
DOI - 10.1002/cssc.201801759
Subject(s) - electrochemistry , delamination (geology) , dimethyl sulfoxide , materials science , electrode , analytical chemistry (journal) , capacitance , chemistry , organic chemistry , paleontology , biology , subduction , tectonics
Functional groups in two‐dimensional (2D) Ti 3 C 2 T x MXene are an important factor influencing electrochemical performance in many applications involving energy storage, electrochemical sensors, and water purification. However, after dimethyl sulfoxide (DMSO) delamination, the effect of surface functionalities in Ti 3 C 2 T x is still unclear and there are no systematic reports on its capacitive behavior. Experiments and theoretical calculations confirm the relationship between different surface functionalities, the DMSO delamination effect, and the electrochemical behavior of the DMSO‐delaminated Ti 3 C 2 T x . The dominant −O and −OH terminations are attributed for surfaces delaminated by using HF [Ti 3 C 2 T x (HF)] and LiF/HCl [Ti 3 C 2 T x (LiF/HCl)], respectively. Theoretical results are also in agreement with experimental results in that −OH terminations are essential for the formation of a free‐standing film. Compared to non‐delaminated Ti 3 C 2 T x (HF) (similar O/F ratios of 1.37 and 1.42), there is a significant DMSO delamination effect for Ti 3 C 2 T x (LiF/HCl) because of different O/F ratios of 2.9 and 3.6. Additionally, the delaminated Ti 3 C 2 T x (LiF/HCl) electrodes deliver a higher capacitance of 508 F cm −3 than that of 333 F cm −3 for the delaminated Ti 3 C 2 T x (HF), although it exhibited lower equivalent series resistance, lower interlayer spacing, and slightly lower specific surface area. This study provides direct and systematic experimental evidence for different functional groups in Ti 3 C 2 T x MXene based on the DMSO delamination effect.