In situ AFM investigation of 2D nucleation on the (100) face of KDP
Author(s) -
Min Cheng,
Mingwei Li,
Yachao Cao,
Xiaoding Wang,
Jinli Guo
Publication year - 2009
Publication title -
crystal research and technology
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.377
H-Index - 64
eISSN - 1521-4079
pISSN - 0232-1300
DOI - 10.1002/crat.200900460
Subject(s) - supersaturation , nucleation , coalescence (physics) , dissolution , chemical physics , crystallography , anisotropy , chemistry , hillock , atomic force microscopy , crystal growth , materials science , nanotechnology , optics , physics , organic chemistry , astrobiology , composite material
Surface morphology of the (100) face of potassium dihydrogen phosphate (KDP) crystals which were grown at different supersaturations at 25 °C was investigated by in situ atomic force microscopy (AFM). Various AFM images of 2D nucleation under different growth conditions were presented. It is found that the growth of KDP is controlled by polynuclear nucleation mechanism at the high supersaturation. With reduction of the supersaturation, the growth velocity of 2D nuclei becomes very slow and shows typical anisotropy. It is found that the process of coalescence of 2D nuclei does not lead to defect. The experiments show that the growth mechanism for KDP at 25 °C changes between step flow and 2D nucleation in the supersaturation range of 4.5‐5%. The triangular nuclei which are close to equilateral triangle are observed in the experiment at the supersaturation σ = 6% for the first time, showing typical anisotropic growth. Through observing the dissolution of 2D nuclei, the dissolving process can be regarded as the reverse process of growth. We also find that the microcrystals landing on the surface at σ = 9% would grow and coalesce with each other and there is no observable defect in the coalescence. (© 2009 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)