Premium
Growth of cadmium zinc telluride by liquid phase electroepitaxy
Author(s) -
Armour N.,
Sheibani H.,
Dost S.
Publication year - 2006
Publication title -
crystal research and technology
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.377
H-Index - 64
eISSN - 1521-4079
pISSN - 0232-1300
DOI - 10.1002/crat.200610701
Subject(s) - cadmium telluride photovoltaics , cadmium zinc telluride , dissolution , tellurium , crucible (geodemography) , electromigration , crystal growth , glovebox , phase (matter) , materials science , chemistry , nanotechnology , metallurgy , crystallography , electrical engineering , composite material , computational chemistry , organic chemistry , detector , engineering
This study was undertaken to examine the feasibility of growing CdZnTe by liquid phase electroepitaxy. Based on our successful LPEE system of GaInAs, a new crucible to grow CdZnTe was developed. The development presented numerous difficulties. The physical properties of CdZnTe make this material very difficult to grow. All components of the system were investigated. Electromigration of the solute across the solution carries species towards the growth interface. In liquid Cd‐Zn‐Te, the CdTe and ZnTe species remain associated, contrary to the GaInAs system. Experiments showed that LPEE growth of CdZnTe is possible and the electromigration mechanism functions well in the CdZnTe solution. Despite this, other problems remained with the new LPEE system. The preparation of the solution proved difficult without pressurizing the LPEE crucible. Control of the reaction required the use of pre‐compounded CdTe and ZnTe. Proper control of the solution saturation is imperative to ensure minimal dissolution of the seed prior to growth initiation and a reasonable growth rate during growth. The solution remained an issue during the duration of growth due to the high vapor pressures of the constituents. Tellurium evaporation during growth could lower solution volume until electrical contact across the solution is broken. Careful preparation of appropriate solution volume was imperative for successful growth. In LPEE, a uniform electric current passage across the growth interface is necessary for uniform and stable growth interface. This requires the design of a uniform contact zone between the bottom graphite electrode and the seed crystal. The contact zone issue was not adequately resolved in this study. However, a number of successful growth runs were achieved despite the electrical contact problems. Results show that the LPEE of growth CdZnTe is feasible. (© 2006 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)