Synthesis and Properties of New Fluorinated Polyimides Derived from an Unsymmetrical and Noncoplanar Diamine
Author(s) -
Wang Chenyi,
Zhao Xiaoyan,
Li Guang
Publication year - 2012
Publication title -
chinese journal of chemistry
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 1.28
H-Index - 41
eISSN - 1614-7065
pISSN - 1001-604X
DOI - 10.1002/cjoc.201200431
Subject(s) - diamine , chemistry , polyimide , ether , trifluoromethyl , glass transition , thermal stability , imide , polymer chemistry , condensation polymer , dielectric , nitrogen , organic chemistry , polymer , materials science , alkyl , optoelectronics , layer (electronics)
Abstract A new unsymmetrical and noncoplanar diamine containing trifluoromethyl and trimethyl groups, 1,4‐bis(4‐amino‐2‐trifluoromethylphenoxy)‐2,3,5‐trimethylbenzene ( 2 ), was synthesized using 2,3,5‐trimethylhydroquinone and 2‐chloro‐5‐nitrobenzotrifluoride as starting materials. A series of fluorinated poly(ether imide)s (PEIs) ( 4a–4d ) were prepared from diamine 2 with four aromatic dianhydrides via a one‐step high‐temperature polycondensation procedure. The obtained PEIs were readily soluble in most organic solvents and could be solution‐cast into flexible and strong films. The resulting thin films exhibited light color and good optical transparency with a cutoff wavelength of 356–376 nm. They also displayed good thermal stability with glass transition temperatures ( T g ) above 281°C, 10% weight loss temperatures in the range of 482–486°C, and the weight residue more than 55% at 800°C in nitrogen. Moreover, they revealed low dielectric constants (2.77–2.93 at 1 MHz) and low moisture absorptions (0.41%–0.57%).