Fe−N 3 /C Active Catalytic Sites for the Oxygen Reduction Reaction Prepared with Molecular‐Level Geometry Control through the Covalent Immobilization of an Iron−Terpyridine Motif onto Carbon
Author(s) -
Fruehwald Holly M.,
Ebralidze Iraklii I.,
Zenkina Olena V.,
Easton E. Bradley
Publication year - 2019
Publication title -
chemelectrochem
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 1.182
H-Index - 59
ISSN - 2196-0216
DOI - 10.1002/celc.201801842
Subject(s) - catalysis , terpyridine , chemistry , x ray photoelectron spectroscopy , thermogravimetric analysis , ligand (biochemistry) , metal , pyrolysis , inorganic chemistry , chemical engineering , organic chemistry , biochemistry , receptor , engineering
A model for a non‐precious metal catalyst for the oxygen reduction reaction (ORR) in aqueous media has been prepared by functionalizing a commercial Vulcan XC‐72 carbon support with a terpyridine‐based nitrogenous ligand. The terpyridine ligand geometry allows the formation of active catalytic sites by selectively embedding a N 3 /C structural motif into the carbon support confirmed by using thermogravimetric analysis (TGA) and X‐ray photoelectron spectroscopy (XPS) measurements. Room‐temperature metal–ligand coordination results in the desired Fe−N 3 /C moieties on the surface. This model system was used to demonstrate the catalytic activity of the surfaces containing mainly Fe−N 3 sites for the ORR in acidic and basic media. Importantly, we demonstrate that the system could be prepared under mild reaction conditions, does not require high‐ temperature treatments, and shows catalytic activity for the ORR. Interestingly, when the system was pyrolyzed in an N 2 atmosphere at 700 °C the resulting activity declined. The non‐heat‐treated Fe−N 3 /C surface demonstrates comparable activity in acidic electrolyte medium when compared to most literature catalysts that are typically heat treated to produce four nitrogen atoms coordinated to one iron center (Fe−N 2+2 /C). Interestingly, despite the fact that many systems reported so far in the literature exhibit enhanced activity after heat treatment, our system showed an increase in activity when the material was not pyrolyzed.