Biomimetic repeat protein derived from Xenopus tropicalis for fibrous scaffold fabrication
Author(s) -
Kwon Yunkyeoung,
Yang Yun Jung,
Jung Dooyup,
Hwang Byeong Hee,
Cha Hyung Joon
Publication year - 2015
Publication title -
biopolymers
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.556
H-Index - 125
eISSN - 1097-0282
pISSN - 0006-3525
DOI - 10.1002/bip.22735
Subject(s) - microfiber , polylactic acid , chemistry , tissue engineering , electrospinning , nanofiber , elastin , fiber , scaffold , xenopus , ultimate tensile strength , biophysics , polymer , biochemistry , nanotechnology , materials science , biomedical engineering , composite material , biology , genetics , medicine , organic chemistry , gene
Collagen, silk, and elastin are the fibrous proteins consist of representative amino acid repeats. Because these proteins exhibited distinguishing mechanical properties, they have been utilized in diverse applications, such as fiber‐based sensors, filtration membranes, supporting materials, and tissue engineering scaffolds. Despite their infinite prevalence and potential, most studies have only focused on a few repeat proteins. In this work, the hypothetical protein with a repeat motif derived from the frog Xenopus tropicalis was obtained and characterized for its potential as a novel protein‐based material. The codon‐optimized recombinant frog repeat protein, referred to as ‘xetro’, was produced at a high rate in a bacterial system, and an acid extraction‐based purified xetro protein was successfully fabricated into microfibers and nanofibers using wet spinning and electrospinning, respectively. Specifically, the wet‐spun xetro microfibers demonstrated about 2‐ and 1.5‐fold higher tensile strength compared with synthetic polymer polylactic acid and cross‐linked collagen, respectively. In addition, the wet‐spun xetro microfibers showed about sevenfold greater stiffness than collagen. Therefore, the mass production potential and greater mechanical properties of the xetro fiber may result in these fibers becoming a new promising fiber‐based material for biomedical engineering. © 2015 Wiley Periodicals, Inc. Biopolymers 103: 659–664, 2015.