Luminescence analysis of SrGa 2 Si 2 O 8 : RE 3+ (RE = Dy, Tm) phosphors
Author(s) -
R.Kadukar Monali,
Dhoble S. J.,
Sahu A. K.,
Nayar V.,
Sailaja S.,
Reddy B. Sudhakar
Publication year - 2017
Publication title -
luminescence
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.428
H-Index - 45
eISSN - 1522-7243
pISSN - 1522-7235
DOI - 10.1002/bio.3161
Subject(s) - phosphor , thermoluminescence , photoluminescence , luminescence , analytical chemistry (journal) , mechanoluminescence , materials science , doping , ion , emission spectrum , spectral line , optoelectronics , chemistry , physics , chromatography , astronomy , organic chemistry
This article reports on the luminescence properties of rare earth (Dy 3 + and Tm 3 + )ions doped SrGa 2 Si 2 O 8 phosphor were studied. SrGa 2 Si 2 O 8 phosphors weresynthesizedby employing solid state reaction method.From the measured X‐ray diffraction (XRD) pattern of the samplemonoclinic phase structure has been observed. Thermoluminescenceand Mechanoluminescence properties of the γ‐ray irradiated samples have been studied. Photoluminescence spectra of Dy 3 + activated SrGa 2 Si 2 O 8 phosphor has been measured with an excitation wavelength at 348 nm,and it shows two emission bands at 483 and 574 nm due to 4 F 9 /2  →  6 H 15 /2 and 4 F 9 /2  →  6 H 13 /2 transitions respectively. Whereas the photoluminescence spectra of Tm 3 + activated SrGa 2 Si 2 O 8 phosphor has been measured with an excitation wavelength at 359 nm and it exhibits two emission bands at 454 and 472 nm due to 1 D 2  →  3 F 4 and 1 G 4  →  3 H 6 transitions respectively. In thermoluminescence study, γ‐irradiatedthermoluminescence glow curve of SrGa 2 Si 2 O 8 :Dy 3 + phosphor shows two well defined peaks at 293 °C (peak1)and 170 °C (peak2) whereas thermoluminescence glow curve of SrGa 2 Si 2 O 8 :Tm 3 + phosphor shows peaks at 292 °C (peak1) and 184 °C (peak2) indicating that two sets of traps are being activated within the particular temperature range and the trapping parameters associated with the prominent glow peaks of SrGa 2 Si 2 O 8 :Dy 3 + and SrGa 2 Si 2 O 8 :Tm 3 + are calculated using Chen's peak shape and initial rise method.From the Mechanoluminescence study, only one glow peak has been observed. Copyright © 2016 John Wiley & Sons, Ltd.