Influence of crystallization on microcellular foaming behavior of polyamide 6 in a supercritical CO 2 ‐assisted route
Author(s) -
Han Shuo,
Jiang Can,
Yu Kesong,
Mi Jianguo,
Chen Shihong,
Wang Xiangdong
Publication year - 2020
Publication title -
journal of applied polymer science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.575
H-Index - 166
eISSN - 1097-4628
pISSN - 0021-8995
DOI - 10.1002/app.49183
Subject(s) - supercritical fluid , materials science , polyamide , crystallization , blowing agent , saturation (graph theory) , composite material , chemical engineering , foaming agent , porosity , organic chemistry , polyurethane , chemistry , mathematics , combinatorics , engineering
Supercritical CO 2 as a blowing agent has attracted increasing interest in the preparation of microcellular polyamide 6 (PA6) foams. In this work, we developed the supercritical CO 2 ‐assisted method to prepare a series of different microcellular PA6 foams by controlling its crystallization properties in two steps and carefully investigated the corresponding crystallization properties of modified PA6 and foams using various techniques. Initially, a multifunctional epoxy‐based chain extender (CE) was used to produce high‐melt strength‐modified PA6 with improved foaming ability; then, the resulting PA6 was foamed to prepare the microcellular foams of PA6 using supercritical CO 2 as a blowing agent in a batch foaming route. The CE effectively enhanced the melt strength of PA6, and CE usage was optimized to obtain a threshold of high branching without crosslinking. The number of crystals was also adjusted by the saturation temperature. Furthermore, these crystals that formed during the saturation process served as high‐efficiency bubble nucleating agents and then limited the growth of bubbles at the same time. The microcellular foams of PA6 were successfully obtained with a cell size of 10.0 μm, and cell density of 2.0 × 10 9 cells/cm 3 at the saturation temperature of 225°C.