Hydrolysis and thermal stability of partially hydrolyzed polyacrylamide in high‐salinity environments
Author(s) -
Oliveira Priscila F.,
Costa Josane A.,
Oliveira Luis Fernando S.,
Mota Letícia S.,
Oliveira Leonardo A.,
Mansur Claudia R. E.
Publication year - 2019
Publication title -
journal of applied polymer science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.575
H-Index - 166
eISSN - 1097-4628
pISSN - 0021-8995
DOI - 10.1002/app.47793
Subject(s) - hydrolysis , polyacrylamide , brine , chemistry , aqueous solution , polymer , thermal stability , precipitation , acrylate , polymer chemistry , chemical engineering , chromatography , organic chemistry , monomer , physics , meteorology , engineering
Partially hydrolyzed polyacrylamide (HPAM) is the water‐soluble polymer most often used in flooding applications in the petroleum industry. However, in aqueous solutions at high temperatures, HPAM undergoes hydrolysis of the lateral amide groups, and the presence of salts in the solution can lead to precipitation of this polymer. Therefore, a method was developed to monitor the thermal stability of HPAM solutions in different saline environments and varying temperatures. The proposed test method involved measurements of intrinsic viscosity as a function of time and determination of the degree of hydrolysis of the HPAM by elemental analysis. The results obtained indicated that the presence of divalent cations (Ca +2 and Mg +2 ) negatively influenced the intrinsic viscosity of the solutions and in some systems led to precocious precipitation of the polymer in environments with higher concentrations of these cations. The hydrolysis reaction of the amide groups to the acrylate groups of the HPAM chain was significantly affected by rising temperature: at 50 °C, hydrolysis occurred, but not as significantly as at 70, 85, 90, and 95 °C. Hydrolysis up to 84% was observed for solutions processed at 90 °C. The results also indicated limits of hardness for the brine at some temperatures: 1353 ppm for 95 °C and 2867 ppm for 70 °C. For brine containing 13,610 ppm or more of divalent cations, hydrolysis and precipitation of the polymer were not observed at 50 °C. © 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019 , 136 , 47793.