Toughening polylactide with epoxidized styrene–butadiene impact resin: Mechanical, morphological, and rheological characterization
Author(s) -
Wang Yanshai,
Wei Zhiyong,
Li Yang
Publication year - 2018
Publication title -
journal of applied polymer science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.575
H-Index - 166
eISSN - 1097-4628
pISSN - 0021-8995
DOI - 10.1002/app.46058
Subject(s) - ultimate tensile strength , materials science , composite material , izod impact strength test , toughness , elongation , styrene butadiene , copolymer , styrene , polymer
Styrene–butadiene impact resin (SBC) was chosen as the toughening agent to improve the tensile toughness of polylactide (PLA). Epoxidized SBC (ESBC) with different epoxidation degree were prepared by epoxidation using in situ peroxoformic acid method and a series of PLA/SBC(ESBC) blends were prepared by melt blending. The elongation at break of the PLA/ESBC blends was greatly improved, which was reflected in the slight decrease in the tensile strength and tensile modulus. Moreover, the tensile strength and tensile modulus were not significantly affected by the epoxidation degree of ESBC. For example, the incorporation of ESBC28.8% (30 wt %) to PLA caused an obvious increment of elongation at break from 3.5% of pure PLA to 305.0%, while the tensile modulus and tensile strength decreased to 80 and 78% of pure PLA, respectively. Scanning electron microscopy observations of cryo‐fractured surface morphology and particle size analysis demonstrated that the compatibility of the PLA/ESBC blends was improved significantly compared to PLA/SBC blend. PLA/ESBC(70/30) blends exhibited shear‐thinning behavior over the range of the studied shear rate. With an increase in shear rate, the non‐Newtonian index of the blends decreased gradually. Furthermore, the flow behavior of PLA/ESBC(70/30) blends was more sensitive to the shear rate than pure PLA. © 2017 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2018 , 135 , 46058.