Comparison of cellulose and chitin nanocrystals for reinforcing regenerated cellulose fibers
Author(s) -
Chen JingHuan,
Liu JinGang,
Yuan TongQi,
Sun RunCang
Publication year - 2017
Publication title -
journal of applied polymer science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.575
H-Index - 166
eISSN - 1097-4628
pISSN - 0021-8995
DOI - 10.1002/app.44880
Subject(s) - regenerated cellulose , materials science , cellulose , crystallinity , spinning , ultimate tensile strength , nanocrystal , thermal stability , dissolution , chemical engineering , nanofiber , composite material , cellulose fiber , chitin , fiber , polymer chemistry , chitosan , nanotechnology , engineering
In this study, regenerated cellulose fibers reinforced by cellulose nanocrystals (CENC) and chitin nanocrystals (CHNC) were prepared by blending the nanocrystals suspensions with the cellulose solution in NaOH/urea/water solvent at room temperature. The effect of nanocrystals' addition on the properties of spinning dopes and regenerated fibers were investigated and compared. Results showed that the obtained CENC and CHNC had different dimensions, and both of them increased the viscosity and decreased the transparency of the spinning dopes. However, the dissolution state of cellulose was not changed. CHNC had a greater influence on the properties of spinning dopes, while CENC had more obvious effect on the performance of regenerated fibers. The CENC reinforced fibers showed a higher crystallinity index as compared to the CHNC reinforced fibers. The tensile strength of the regenerated fibers was evidently improved when 3 wt % CENC or 2 wt % CHNC were added, while the elongation at break of the fibers was slightly decreased with the increase of nanocrystals content. The morphology and thermal stability of the regenerated fibers was not affected by the addition of nanocrystals. This study suggested that the dimension, group and content of nanocrystals were important factors for the reinforcement of regenerated cellulose fibers. © 2017 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2017 , 134 , 44880.