Premium
Relaxation behavior and activation energy of relaxation for polyimide and polyimide–graphene nanocomposite
Author(s) -
Marashdeh Wajeeh F.,
Longun Jimmy,
Iroh Jude O.
Publication year - 2016
Publication title -
journal of applied polymer science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.575
H-Index - 166
eISSN - 1097-4628
pISSN - 0021-8995
DOI - 10.1002/app.43684
Subject(s) - polyimide , activation energy , materials science , glass transition , nanocomposite , arrhenius equation , composite number , relaxation (psychology) , composite material , graphene , dynamic mechanical analysis , polymer chemistry , atmospheric temperature range , polymer , analytical chemistry (journal) , thermodynamics , chemistry , nanotechnology , organic chemistry , physics , psychology , social psychology , layer (electronics)
The relaxation behavior of polyimide and its nanocomposite containing 10 wt % of graphene was studied by using the dynamic mechanical spectrometer. Dynamic mechanical analysis of polyimide and its composite was performed as a function of temperature and frequency in the temperature range of 25–480 °C and frequency range between 0.05 and 100 Hz. The effect of increasing frequency of testing from 0.05 to 100 Hz is a significant shift from the glass transition temperature, T g , to higher temperature from 360 °C at 0.05 Hz to 420 °C at 100 Hz. The tan δ peak height for both α and β transitions decreased with increasing test frequency from 0.24 at 0.05 Hz to 0.08 at 100 Hz, due to increasing restriction to chain motion. At any given testing frequency, the T g for the composite was shown to be higher than that for the matrix by about 5–10 °C. The Arrhenius equation was used to calculate the activation energy for both α and β transitions. The activation for α and β transitions for the composite and polyimide matrix were determined to be 688 and 537 kJ/mol and 313 and 309 kJ/mol, respectively, indicating that a significant increase in the energy barrier to chain relaxation occurred as a result of reinforcement of polyimide with low weight fraction of graphene. © 2016 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2016 , 133 , 43684.