High‐temperature‐resistant polymer gel system with metal–organic mixed cross‐linking agents
Author(s) -
Zhang Xiaoyun,
Zhang Sisi,
Li Liang,
Wu Ruonan,
Liu Dongming,
Wu Jihui,
Wu Wei
Publication year - 2015
Publication title -
journal of applied polymer science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.575
H-Index - 166
eISSN - 1097-4628
pISSN - 0021-8995
DOI - 10.1002/app.42261
Subject(s) - polymer , materials science , polyacrylamide , thermal stability , scanning electron microscope , chemical engineering , formaldehyde , rheology , polymer chemistry , chemistry , composite material , organic chemistry , engineering
A high‐temperature (200°C)‐resistant polymer gel system was developed from partially hydrolyzed polyacrylamide (HPAM), chromium lactate (CrL), and water‐soluble phenol/formaldehyde resin (WPF) mixed cross‐linkers. Rheological measurements indicated that the gelation process of the gel system could be divided into four successive steps: induction, first cross‐linking with metal cross‐linker, secondary cross‐linking with organic cross‐linker, and stabilization. Effects of various parameters that affect the gelation time and gel strength including polymer concentration, cross‐linker concentration, salinity, pH, and the gelation temperature were evaluated. Gelant formulated with 0.5 wt % HPAM, 0.1 wt % CrL, and 0.9 wt % WPF and treated at 80°C for 48 h showed sufficient gelation time, high rigidity, and good thermal stability. Morphology observation by scanning electron microscopy (SEM) and atomic force microscopy (AFM) revealed that the gel had compact network microstructure. A cross‐linking mechanism for the gel system was proposed based on the gelation process and experimental results. © 2015 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2015 , 132 , 42261.