Electrical and thermal conductivity and tensile and flexural properties: Comparison of carbon black/polycarbonate and carbon nanotube/polycarbonate resins
Author(s) -
King Julia A.,
Via Michael D.,
King Michelle E.,
Miskioglu Ibrahim,
Bogucki Gregg R.
Publication year - 2011
Publication title -
journal of applied polymer science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.575
H-Index - 166
eISSN - 1097-4628
pISSN - 0021-8995
DOI - 10.1002/app.33890
Subject(s) - polycarbonate , materials science , composite material , carbon black , ultimate tensile strength , flexural strength , electrical resistivity and conductivity , carbon nanotube , composite number , percolation threshold , flexural modulus , conductivity , chemistry , natural rubber , electrical engineering , engineering
Adding conductive carbon fillers to thermoplastic polymers increases the resulting composite's electrical conductivity. Carbon black (CB) is very effective at increasing composite electrical conductivity at low loading levels. In this study, varying amounts (2 to 10 wt %) CB were added to polycarbonate (PC) and the resulting composites were tested for electrical conductivity (1/electrical resistivity), thermal conductivity, and tensile and flexural properties. These results were compared with prior work done for carbon nanotubes (CNT) in polycarbonate. The percolation threshold was ∼ 2.3 vol % CB compared to between 0.7 and 1.4 vol % CNT. At 8 wt % filler, the CNT/PC composite had an electrical resistivity of 8 ohm‐cm compared to 122 ohm‐cm for the CB/PC composite. The addition of CB to polycarbonate increased the composite electrical and thermal conductivity and tensile and flexural modulus. The 8 wt % (5.5 vol %) CB in polycarbonate composite had a good combination of properties for semiconductive applications. Ductile tensile behavior is noted in pure polycarbonate and in samples containing up to 8 wt % CB. © 2011 Wiley Periodicals, Inc. J Appl Polym Sci, 2011