A new Schiff base epoxy oligomer resin: Synthesis, characterization, and thermal decomposition kinetics
Author(s) -
Kaya İsmet,
Doğan Fatih,
Gül Murat
Publication year - 2011
Publication title -
journal of applied polymer science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.575
H-Index - 166
eISSN - 1097-4628
pISSN - 0021-8995
DOI - 10.1002/app.33843
Subject(s) - thermogravimetry , thermogravimetric analysis , thermal decomposition , oligomer , polymer chemistry , materials science , gel permeation chromatography , kinetics , schiff base , chemistry , organic chemistry , inorganic chemistry , composite material , polymer , physics , quantum mechanics
Oligo{2,2′‐{1,4‐phenylenebis[nitrilomethylylidene]}bis(6‐methoxyphenol)} (OPNMMP) was synthesized from o ‐vanillin and p ‐phenylene diamine by oxidative polycondensation with NaOCl in an aqueous alkaline. Then, a new Schiff Base epoxy oligomer resin, OPNMMP–epichlorohydrine (EPC), was produced with EPC. The structures of the resulting compounds were confirmed by Fourier transform infrared spectroscopy, ultraviolet–visible spectroscopy, 1 H‐NMR, and 13 C‐NMR. Further characterization processes were preformed by thermogravimetry (TG)–differential thermal analysis, gel permeation chromatography, and solubility testing. Also, the kinetics of the thermal decomposition of OPNMMP–EPC were investigated by thermogravimetric analysis. The TG curves showed that the thermal decomposition of OPNMMP–EPC occurred in one stage. The kinetic parameters related to the decomposition kinetics of OPNMMP–EPC were obtained from TG curves with the following methods: Friedman, Flynn–Wall–Ozawa, Kissinger, invariant kinetic parameter, and Coats–Redfern (CR), under an N 2 dynamic atmosphere and different heating rates (5, 10, 15, and 20°C/min). The mechanism function and pre‐exponential factor were also determined by a master plots method. The apparent activation energies of the thermal decomposition were calculated from these methods for OPNMMP–EPC. The analysis of the results obtained by the CR and master plots methods showed that the decomposition mechanism of OPNMMP–EPC in N 2 was a deceleration‐type mechanism. © 2011 Wiley Periodicals, Inc. J Appl Polym Sci, 2011