Effect of nucleation agents on the crystallization of poly(3‐hydroxybutyrate‐ co ‐4‐hydroxybutyrate) (P3/4HB)
Author(s) -
Wang Liang,
Wang Xiaojuan,
Zhu Wenfu,
Chen Zhifei,
Pan Jueyu,
Xu Kaitian
Publication year - 2009
Publication title -
journal of applied polymer science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.575
H-Index - 166
eISSN - 1097-4628
pISSN - 0021-8995
DOI - 10.1002/app.31588
Subject(s) - crystallization , nucleation , talc , materials science , chemical engineering , boron nitride , zinc stearate , polymer chemistry , chemistry , composite material , organic chemistry , raw material , engineering
Boron nitride (BN), talc, hydroxyapatite (HA), and zinc stearate (ZnSt) were investigated as nucleation agents (NA) for nonfossil‐based poly(3‐hydroxybutyrate‐ co ‐4‐hydroxybutyrate) (P3/4HB) plastics. Nonisothermal crystallization behaviors of the P3/4HB/NA blends were examined by DSC. It revealed that BN is the most efficient nucleation agent to promote the crystallization rate, however, but not the crystallization degree. The lasting crystallization of P3/4HB was also removed. The nucleation effect was strengthened with increase of BN content up to 1% and then slackened deeply when further BN was added. Isothermal crystallization analysis revealed that the addition of nucleation agent BN does not alter the crystal growth mode of P3/4HB, with maintaining the Avrami parameter n value around 2.40. Talc did enhance the crystallization of P3/4HB with however milder crystal growth rate. HA and ZnSt did not promote, but depressed the crystallization of P3/4HB plastics. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2010