Effects of solvent basicity on free radical polymerizations of N , N ′‐bismaleimide‐4,4′‐diphenylmethane initiated by barbituric acid
Author(s) -
Su HengLei,
Hsu JungMu,
Pan JingPin,
Wang TsungHsiung,
Chern ChorngShyan
Publication year - 2010
Publication title -
journal of applied polymer science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.575
H-Index - 166
eISSN - 1097-4628
pISSN - 0021-8995
DOI - 10.1002/app.31297
Subject(s) - diphenylmethane , polymer chemistry , chemistry , solvent , polymerization , molar mass , radical polymerization , polymer , ketone , anionic addition polymerization , catalysis , organic chemistry
Abstract The polymerizations of N , N ′‐bismaleimide‐4,4′‐diphenylmethane (BMI) initiated by barbituric acid (BTA) carried out in a variety of solvents at 130°C were studied. The nitrogen‐containing cyclic solvents such as N ‐methyl‐2‐pyrrolidinone acted as a catalyst to promote the formation of the three‐dimensional crosslinked network structure. By contrast, the polymerization in a cyclic solvent that did not contain nitrogen such as γ‐butyrolactone resulted in nil gel content. The higher the solvent basicity, the larger the amount of insoluble polymer species formed. The molar ratio of BTA to BMI also played an important role in the polymerizations. The resultant polymers, presumably having a hyper‐branched structure, exhibited much narrower molecular weight distributions than those prepared by conventional free radical polymerizations. The BMI polymerizations using BTA as the initiator could not be adequately described by conventional free radical polymerization mechanisms. A polymerization mechanism that took into account the generation of a ketone radical pair between BTA and BMI and the subsequent initiation, propagation and termination reactions was proposed. It was concluded that the nitrogen‐containing cyclic solvents were capable of participating in the ketone radical pair formation process, thereby increasing the extent of polymer crosslinking reactions. © 2010 Wiley Periodicals, Inc. J Appl Polym Sci, 2010