Synthesis and characterization of novel fluorine‐containing methacrylate copolymers: Reactivity ratios, thermal properties, and antimicrobial activity
Author(s) -
Erol Ibrahim,
Sen Ozkan,
Dedelioglu Ayse,
Cifci Cemal
Publication year - 2009
Publication title -
journal of applied polymer science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.575
H-Index - 166
eISSN - 1097-4628
pISSN - 0021-8995
DOI - 10.1002/app.30835
Subject(s) - copolymer , polymer chemistry , reactivity (psychology) , monomer , thermogravimetric analysis , mole fraction , thermal stability , gel permeation chromatography , methacrylate , dispersity , glass transition , polymer , materials science , chemistry , organic chemistry , medicine , alternative medicine , pathology
The free‐radical‐initiated copolymerization of 2‐(4‐acetylphenoxy)‐2‐oxoethyl‐2‐methylacrylate (AOEMA) and 2‐(4‐benzoylphenoxy)‐2‐oxoethyl‐2‐methylacrylate (BOEMA) with 2‐[(4‐fluorophenyoxy]‐2‐oxoethyl‐2‐methylacrylate (FPEMA) were carried out in 1,4‐dioxane solution at 65°C using 2,2′‐azobisisobutyronitrile as an initiator with different monomer‐to‐monomer ratios in the feed. The monomers and copolymers were characterized by FTIR and 1 H‐ and 13 C‐NMR spectral studies. 1 H‐NMR analysis was used to determine the molar fractions of AOEMA, BOEMA, and FPEMA in the copolymers. The reactivity ratios of the monomers were determined by the application of Fineman‐Ross and Kelen‐Tudos methods. The analysis of reactivity ratios revealed that BOEMA and AOEMA are less reactive than FPEMA, and copolymers formed are statistically in nature. The molecular weights ( M w and M n ) and polydispersity index of the polymers were determined using gel permeation chromatography. Thermogravimetric analysis of the polymers reveals that the thermal stability of the copolymers increases with an increase in the mole fraction of FPEMA in the copolymers. Glass transition temperatures of the copolymers were found to decrease with an increase in the mole fraction of FPEMA in the copolymers. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2009