Dynamic vulcanization of polyethylene‐based thermoplastic elastomer blends
Author(s) -
Sarkhel Gautam,
Choudhury Arup
Publication year - 2009
Publication title -
journal of applied polymer science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.575
H-Index - 166
eISSN - 1097-4628
pISSN - 0021-8995
DOI - 10.1002/app.30285
Subject(s) - vulcanization , materials science , ethylene propylene rubber , polyethylene , composite material , curing (chemistry) , copolymer , natural rubber , elastomer , thermoplastic elastomer , thermoplastic , ethylene , polymer blend , epdm rubber , polymer , polymer chemistry , organic chemistry , chemistry , catalysis
In this investigation, the effects of blending with ethylene–propylene–diene terpolymer and subsequent dynamic curing with sulfur on the macromolecular structure and properties of pure low‐density polyethylene and high‐density polyethylene were studied. The crosslinking efficiency of polyethylene‐based ethylene–propylene–diene terpolymer blends upon dynamic curing was assessed with torque and gel content measurements. The curing of dispersed ethylene–propylene–diene terpolymer in a polyethylene matrix improved both the mechanical and thermomechanical properties as a result of the formation of a crosslink structure in the rubber phase. In view of the electrical applications of this cured blend material, the volume resistivity was measured. The thermal stability of vulcanized polyethylene/ethylene–propylene–diene terpolymer blends was found to be superior to that of unvulcanized blends. In scanning electron microscopy analysis, good interface bonding between the polyethylene matrix and dispersed ethylene–propylene–diene terpolymer was observed for the cured blends. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2010