Boger A.,
Imhof C.,
Heise B.,
Marti O.,
Troll C.,
Rieger B.,
Hild S.
Publication year - 2008
Publication title -
journal of applied polymer science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.575
H-Index - 166
eISSN - 1097-4628
pISSN - 0021-8995
DOI - 10.1002/app.29282
Subject(s) - tacticity , materials science , microstructure , amorphous solid , composite material , polymer , small angle x ray scattering , polypropylene , deformation (meteorology) , scattering , crystallography , polymerization , optics , chemistry , physics
Novel asymmetric metallocene catalysts lead to low isotactic polypropylenes (iPP) with randomly distributed stereo irregularities. The polypropylenes are low crystalline and show elastic mechanical behavior due to physical crosslinking. The morphology of such iPP, which is responsible for the observed mechanical properties, is still sparsely resolved. In the present work a low isotactic, low crystalline metallocene iPP containing randomly distributed stereoerrors was investigated. The influence of the chain microstructure in the elastic properties was studied using two complementary investigation methods, X‐ray diffraction and scanning force microscopy (SFM). For a better understanding of the unique mechanical properties, microscopic changes in morphology and strain‐induced variation in chain orientation were monitored during uniaxial stretching using SFM and wide angle X‐ray scattering measurements. For quantitative analysis and discussion the polymer chain orientations were calculated. The correlation between the orientation, the arrangements of the amorphous and crystalline phases observed by SFM, and the mechanical properties of the material at different elongation ratios allowed an interpretation of the macroscopic behavior on the microscopic scale. It was shown that the deformation behavior of low isotactic polypropylene with randomly distributed stereoerrors is in agreement with existing structural models, which proposed that small crystalline domains act as physical crosslinks for the amorphous matrix. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2009