Polyoxymethylene/polyurethane/alumina ternary composites: Structure, mechanical, thermal and dielectric properties
Author(s) -
Siengchin S.,
KargerKocsis J.,
Psarras G. C.,
Thomann R.
Publication year - 2008
Publication title -
journal of applied polymer science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.575
H-Index - 166
eISSN - 1097-4628
pISSN - 0021-8995
DOI - 10.1002/app.28589
Subject(s) - materials science , composite material , polyoxymethylene , differential scanning calorimetry , masterbatch , thermogravimetric analysis , dynamic mechanical analysis , boehmite , scanning electron microscope , thermomechanical analysis , nanocomposite , polymer , thermal expansion , chemical engineering , aluminium , engineering , thermodynamics , physics
Abstract Ternary composites composed of polyoxymethylene (POM), polyurethane (PU), and boehmite alumina were produced by melt blending with and without latex precompounding. Latex precompounding served for the predispersion of the alumina particles. The related masterbatch (MB) was produced by mixing the PU latex with water‐dispersible boehmite alumina. The dispersion of the alumina was studied by transmission and scanning electron microscopy techniques (TEM and SEM, respectively) and discussed. The crystallization of POM was inspected by means of differential scanning calorimetry (DSC) and polarized optical microscopy (DSC and polarized light microscopy, respectively). The mechanical and thermomechanical properties of the composites were determined in uniaxial tensile, dynamic‐mechanical thermal analysis (DMTA), short‐time creep tests (performed at various temperatures), and thermogravimetric analysis (TGA). The melt flow of the composites was characterized in a plate/plate rheometer. In addition, the dielectric response of the nanocomposites was investigated by means of broadband dielectric spectroscopy at an ambient temperature. The composites produced by the MB technique outperformed the direct melt (DM) compounded composites in respect to the thermal and mechanical characteristics. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2008