Pilling in cellulosic fabrics, Part 2: A study on kinetics of pilling in alkali‐treated lyocell fabrics
Author(s) -
Bui Huong M.,
Ehrhardt Anelise,
Bechtold Thomas
Publication year - 2008
Publication title -
journal of applied polymer science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.575
H-Index - 166
eISSN - 1097-4628
pISSN - 0021-8995
DOI - 10.1002/app.28570
Subject(s) - lyocell , abrasion (mechanical) , cellulose fiber , materials science , composite material , fiber , tenacity (mineralogy) , chemistry
As pilling in textiles originates from many factors, the kinetic of pilling formation play an important role in the investigation and approaches of pilling. The single jersey‐knitted lyocell fabrics were treated with different alkaline solution concentrations and submitted to Rapid Pilling Test—a wet‐state Martindale test for cellulosic fabrics performed with increasing abrasion cycles. After each type of cycles, the pilling density was microscopically counted, and then pilling was visually rated. The changes in fiber properties were followed by water retention values (WRV), fibers swelling, fiber wet abrasion resistance (NSF), and fibers tenacity/elongation in wet and in dry states. The kinetics of pill formation—quantified by pills/cm 2 —occurred in the following steps: pills are promptly formed at first abrasion cycles, reached the pill plateau cycles, and are self‐removed from the fabric surface. The untreated and alkali‐treated lyocell fabrics followed a similar trend of pill formation. However, the pilling propensity is distinct depending on the concentrations. The changes in the swollen state of fiber properties and fiber–fiber friction mainly determined the pill kinetics in lyocell fabrics. The kinetic model aims to figure out the pilling mechanism and the appropriate treatment for pilling resistance. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2008