Improving low‐density polyethylene/poly(ethylene terephthalate) blends with graft copolymers
Author(s) -
ElNashar D. E.,
Maziad N. A.,
Sadek E. M.
Publication year - 2008
Publication title -
journal of applied polymer science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.575
H-Index - 166
eISSN - 1097-4628
pISSN - 0021-8995
DOI - 10.1002/app.28503
Subject(s) - low density polyethylene , materials science , differential scanning calorimetry , thermogravimetric analysis , compatibilization , copolymer , polymer blend , swelling , polyethylene , composite material , acrylonitrile , scanning electron microscope , ethylene , polymer chemistry , chemical engineering , polymer , organic chemistry , chemistry , catalysis , physics , engineering , thermodynamics
Blends of low‐density polyethylene (LDPE) and poly(ethylene terephthalate) (PET) were prepared with different weight compositions with a plasticorder at 240°C at a rotor speed of 64 rpm for 10 min. The physicomechanical properties of the prepared blends were investigated with special reference to the effects of the blend ratio. Graft copolymers, that is, LDPE‐grafted acrylic acid and LDPE‐grafted acrylonitrile, were prepared with γ‐irradiation. The copolymers were melt‐mixed in various contents (i.e., 3, 5, 7, and 9 phr) with a LDPE/PET blend with a weight ratio of 75/25 and used as compatibilizers. The effect of the compatibilizer contents on the physicomechanical properties and equilibrium swelling of the binary blend was investigated. With an increase in the compatibilizer content up to 7 phr, the blend showed an improvement in the physicomechanical properties and reduced equilibrium swelling in comparison with the uncompatibilized one. The addition of a compatibilizer beyond 7 phr did not improve the blend properties any further. The efficiency of the compatibilizers (7 phr) was also evaluated by studies of the phase morphology (scanning electron microscopy) and thermal properties (differential scanning calorimetry and thermogravimetric analysis). © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2008