Direct fluorination of Twaron fiber and investigation of mechanical thermal and morphological properties of high density polyethylene and Twaron fiber composites
Author(s) -
Maity J.,
Jacob C.,
Das C. K.,
Singh R. P.
Publication year - 2007
Publication title -
journal of applied polymer science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.575
H-Index - 166
eISSN - 1097-4628
pISSN - 0021-8995
DOI - 10.1002/app.27510
Subject(s) - composite material , materials science , fiber , ultimate tensile strength , crystallinity , high density polyethylene , polyethylene , synthetic fiber
Composites consisting of high density polyethylene (HDPE) reinforced with randomly oriented chopped Twaron fibers (both fluorinated and nonfluorinated) show a significant increase in mechanical and thermal properties. To increase the better fiber matrix adhesion, the Twaron fiber is surface fluorinated using elemental fluorine. The surface of the Twaron fiber becomes very rough and the diameter of Twaron fiber increases from ∼ 12 to 14 μm after fluorination. The composites were prepared using solution method to overcome the damage of the fiber. The tensile strength and the Young's modulus increases with increasing fiber content. The tensile strength and modulus of modified fiber (fluorinated Twaron fiber) composites is much higher than nonmodified fiber composites indicating that there is better mechanical interlocking between the modified fiber and the matrix. Thermal properties obtained from DSC and DTA‐TG analysis of the fluorinated fiber composites are also improved. Contact angle measurements, as well as the surface energy measurements, indicate that the composites are more wettable and is maximum for fluorinated fiber composites i.e., surface energy for fluorinated fiber composites is highest. Crystallinity is also higher for fluorinated fiber composites. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 2008