Structure and processability of iodinated poly(vinyl alcohol). IV. Drawability of the films iodinated at solution before casting
Author(s) -
Shin Eun Joo,
Lee Yang Hun,
Choi Suk Chul
Publication year - 2007
Publication title -
journal of applied polymer science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.575
H-Index - 166
eISSN - 1097-4628
pISSN - 0021-8995
DOI - 10.1002/app.26743
Subject(s) - crystallinity , materials science , ultimate tensile strength , polyvinyl alcohol , casting , composite material , elongation , amorphous solid , vinyl alcohol , aqueous solution , modulus , yield (engineering) , polymer , crystallography , chemistry , organic chemistry
The drawability of iodinated at solution before casting (IBC) polyvinyl alcohol films prepared by casting aqueous solutions of 10 wt % PVA containing 15.2, 39.8, 83.2, 117.0, and 140.1% was examined with a tensile tester at 20–60°C. The tensile behavior of IBC films showed that the yield and breaking loads were much lower, and the breaking elongation was even higher than those of the unoriented iodinated after casting (IAC) films as well as the untreated PVA films. The maximum draw ratios of the films with the weight gain of 15.2, 39.8, 83.2, 117, and 140.1% were 4.5, 5.5, 8.5, 8.0, and 7.5, respectively, which were achieved at 20°C in all. The crystallinity of all films increased by the maximum draw, regardless of crystallinity before drawing. The crystalline structure was recovered to the original PVA crystalline lattice by deiodination. Amorphous orientation and initial moduli increased with the maximum draw ratio, while the orientation of crystals was constant. The orientation and moduli increased up to the weight gain of 83.2%, whose highest draw ratio and initial modulus were 8.5 and of 7.1 GPa, respectively, and then decreased. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 2008