Novel adamantane‐containing epoxy resin
Author(s) -
Su Xiaoming,
Jing Xinli
Publication year - 2007
Publication title -
journal of applied polymer science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.575
H-Index - 166
eISSN - 1097-4628
pISSN - 0021-8995
DOI - 10.1002/app.26533
Subject(s) - epoxy , thermogravimetric analysis , diglycidyl ether , materials science , differential scanning calorimetry , polymer chemistry , bisphenol a , glass transition , adamantane , bisphenol , nuclear chemistry , composite material , chemistry , polymer , organic chemistry , physics , thermodynamics
A novel adamantane‐containing epoxy resin diglycidyl ether of bisphenol‐adamantane (DGEBAda) was successfully synthesized from 1,3‐bis(4‐hydroxyphenyl)adamantane by a one‐step method. The proposed structure of the epoxy resin was confirmed with Fourier transform infrared, 1 H‐NMR, gel permeation chromatography, and epoxy equivalent weight titration. The synthesized adamantane‐containing epoxy resin was cured with 4,4′‐diaminodiphenyl sulfone (DDS) and dicyandiamide (DICY). The thermal properties of the DDS‐cured epoxy were investigated with differential scanning calorimetry and thermogravimetric analysis (TGA). The dielectric properties of the DICY‐cured epoxy were determined from its dielectric spectrum. The obtained results were compared with those of commercially available diglycidyl ether of bisphenol A (DGEBA), a tetramethyl biphenol (TMBP)/epoxy system, and some other associated epoxy resins. According to the measured values, the glass‐transition temperature of the DGEBAda/DDS system (223°C) was higher than that of the DGEBA/DDS system and close to that of the TMBP/DDS system. TGA results showed that the DGEBAda/DDS system had a higher char yield (25.02%) and integral procedure decomposition temperature (850.7°C); however, the 5 wt % degradation temperature was lower than that of DDS‐cured DGEBA and TMBP. Moreover, DGEBAda/DDS had reduced moisture absorption and lower dielectric properties. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 2007