Evaluation and characterization of ammoniumpolyphosphate–pentaerythritol‐based systems for intumescent coatings
Author(s) -
Andersson Anna,
Lundmark Stefan,
Maurer Frans H. J.
Publication year - 2007
Publication title -
journal of applied polymer science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.575
H-Index - 166
eISSN - 1097-4628
pISSN - 0021-8995
DOI - 10.1002/app.25588
Subject(s) - intumescent , pentaerythritol , materials science , composite material , rheology , rheometer , carbon fibers , fire retardant , composite number
Intumescent coatings are increasingly used as a method of passive fire protection on steel constructions. By forming a carbon network and releasing a blowing agent, the thin intumescent film swells 100‐fold at elevated temperatures. The highly insulating foam effectively prevents the load bearing steel from reaching its critical temperature at which it looses its mechanical properties and collapses. The role of the carbon donor in intumescent coatings has been studied. Comparison in temperature development, foaming ratios, and rheological behavior has been performed between formulations containing pentaerythritol (penta), di–penta, and tri–penta. A simulated fire test, in which the temperature development during intumescence was studied, showed that the formulations containing penta were considerably more efficient in keeping a low temperature throughout the process. A more rapid temperature development was displayed when using di–penta and tri–penta as the carbon donor. Rheometer tests indicate that penta formulations enter the intumescent process at a lower temperature and stays in it for a longer time than di–penta and tri–penta formulations. Furthermore, the crossover temperature and maximum phase angle are shifted towards higher temperatures by replacing penta with di–penta and with tri–penta in the formulations, respectively. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 104: 748–753, 2007