Kinetics of the effect of ageing on tensile properties of a natural rubber compound
Author(s) -
Ngolemasango E. F.,
Bennett M.,
Clarke Jane
Publication year - 2006
Publication title -
journal of applied polymer science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.575
H-Index - 166
eISSN - 1097-4628
pISSN - 0021-8995
DOI - 10.1002/app.24634
Subject(s) - ageing , ultimate tensile strength , natural rubber , vulcanization , activation energy , materials science , modulus , kinetics , composite material , elongation , chemistry , genetics , physics , quantum mechanics , biology
Natural rubber (NR) undergoes chemical changes on heat and air ageing. These changes affect its physical properties and as such, affect the service life of the rubber compound. In this study, a vulcanized NR compound of a typical engine mount composition was subjected to thermo‐oxidative ageing at temperatures from 70 to 110°C, to assess the effect on the tensile properties. The kinetics of degradation of the rubber compound, in terms of changes in these properties, was investigated. A fractional rate law was used to describe the kinetics of ageing in terms of its effect on modulus. Rates of ageing, in terms of effect on modulus, passed through a minimum at about 80°C, indicating the danger of trying to extrapolate in‐service ageing behavior from high temperature ageing data. The activation energy of ageing in terms of its effect on modulus, determined for temperatures of 90–110°C, was 151 kJ mol −1 . A second order rate law was used to describe the kinetics of ageing in terms of its effect on tensile strength and elongation at break, with activation energies of 88.32 and 74.3 kJ mol −1 , respectively. According to Ahagon's (Ahagon et al., Rubber Chem Technol, 1990, 63, 683) classification of ageing mechanisms, Type I and Type III ageing mechanisms were predominant. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102:3732–3740, 2006