Wood flour: New filler for the rubber processing industry. IV. Cure characteristics and mechanical properties of natural rubber compounds filled by non‐modified or corona treated wood flour
Author(s) -
Vladkova T. G.,
Dineff P. D.,
Gospodinova D. N.,
Avramova I.
Publication year - 2006
Publication title -
journal of applied polymer science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.575
H-Index - 166
eISSN - 1097-4628
pISSN - 0021-8995
DOI - 10.1002/app.23730
Subject(s) - natural rubber , wood flour , composite material , corona discharge , materials science , x ray photoelectron spectroscopy , filler (materials) , oxygen , chemistry , chemical engineering , organic chemistry , electrode , engineering
It is presented here how some cure characteristics and mechanical properties of rubber compounds based on nonpolar rubber, natural rubber (NR), are affected by filling with conifer wood flour, both nonmodified or corona treated in air or in ammonia. The corona treatment was performed at room temperature and varied both: treatment duration and voltage to find out the maximal reinforcing effect of the modified wood flour. The discharge voltage was varied at 10, 12, and 15 kV to include both (1) the range of relative low voltages (lower than 10 ÷ 12 kV in which the major active species arise from ionized and activated air oxygen and (2) the range of relative high voltages (12 kV and higher) in which the active species arise from simultaneously ionized and activated air oxygen and nitrogen. The chemical composition of the nonmodified and corona‐treated wood surface was controlled by X‐ray photoelectron spectroscopy (XPS) analysis. The activity of the modified wood flour was evaluated by comparative measurement of some basic mechanical parameters of rubber compounds, filled at equal level by nonmodified or plasma‐treated wood flour. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 101: 651–658, 2006