Novel organosoluble poly(amide‐imide‐imide)s synthesized from new tetraimide‐dicarboxylic acid by condensation with 4,4′‐oxydiphthalic anhydride, 1,4‐bis(4‐amino‐2‐trifluoromethylphenoxy)benzene, trimellitic anhydride, and various aromatic diamines
Author(s) -
Yang ChinPing,
Chen YaPing,
Woo E. M.
Publication year - 2006
Publication title -
journal of applied polymer science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.575
H-Index - 166
eISSN - 1097-4628
pISSN - 0021-8995
DOI - 10.1002/app.23364
Subject(s) - imide , polymer chemistry , trimellitic anhydride , condensation polymer , thermogravimetric analysis , thermal stability , monomer , polyamide , polyimide , dicarboxylic acid , materials science , triphenyl phosphite , pyridine , glass transition , polymer , chemistry , organic chemistry , layer (electronics)
A new monomer of tetraimide‐dicarboxylic acid (IV) was synthesized by starting from ring‐opening addition of 4,4′‐oxydiphthalic anhydride, trimellitic anhydride, and 1,4‐bis(4‐amino‐2‐trifluoromethylphenoxy)benzene at a 1:2:2 molar ratio in N ‐methyl‐2‐pyrrolidone (NMP). From this new monomer, a series of novel organosoluble poly(amide‐imide‐imide)s with inherent viscosities of 0.7–0.96 dL/g were prepared by triphenyl phosphite activated polycondensation from the tetraimide‐diacid with various aromatic diamines. All synthesized polymers were readily soluble in a variety of organic solvents such as NMP and N , N ‐dimethylacetamide, and most of them were soluble even in less polar m ‐cresol and pyridine. These polymers afforded tough, transparent, and flexible films with tensile strengths ranging from 99 to 125 MPa, elongations at break from 12 to 19%, and initial moduli from 1.6 to 2.4 GPa. The thermal properties and stability were also good with glass‐transition temperatures of 236–276°C and thermogravimetric analysis 10 wt % loss temperatures of 504–559°C in nitrogen and 499–544°C in air. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 101: 2854–2864, 2006