Simultaneous interpenetrating polymer networks based on bromoacrylated castor oil polyurethane
Author(s) -
Eren Tarik,
Çolak Semra,
Küsefoglu Selim H.
Publication year - 2006
Publication title -
journal of applied polymer science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.575
H-Index - 166
eISSN - 1097-4628
pISSN - 0021-8995
DOI - 10.1002/app.22549
Subject(s) - castor oil , acrylate , methacrylate , polyurethane , polymer chemistry , dynamic mechanical analysis , materials science , polymer , thermogravimetric analysis , methyl methacrylate , styrene , chemistry , polymerization , organic chemistry , monomer , composite material , copolymer
In the first part of this study, simultaneous addition of bromine and acrylate to the double bonds of castor oil was achieved. In the second part of the study, bromoacrylated castor oil (BACO) was reacted with toluenediisocyanate (TDI), to form a prepolyurethane (BACOP). The prepolyurethanes were reacted with styrene (STY), 2‐hydroxyethyl methacrylate (HEMA), methyl methacrylate (MMA), and 3‐(acryloxy)‐2‐hydroxy propyl methacrylate (AHPMA) free radically, using the acrylate functional group to prepare the simultaneous interpenetrating polymer networks (SINs). 2,2′‐Azobis (isobutyronitrile) (AIBN) was used as the initiator and diethylene glycol dimethacrylate (DEGDMA) was used as the crosslinker. BACO and BACOP were characterized by IR, 1 H‐NMR, and 13 C‐NMR techniques. Synthesized polymers were characterized by their resistance to chemical reagents, thermogravimetric analysis, and dynamic mechanical thermal analyzer (DMTA). All the polymers decomposed with 6–10% weight loss in a temperature range of 25–240°C. MMA‐type SIN showed the highest T g (126°C), while STY‐type SINs showed the highest storage modulus (8.6 × 10 9 Pa) at room temperature, with respect to other synthesized SINs. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 100: 2947–2955, 2006