Short beam three point bend tests in syntactic foams. Part I: Microscopic characterization of the failure zones
Author(s) -
Shankar Ravi,
Sankaran S.
Publication year - 2005
Publication title -
journal of applied polymer science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.575
H-Index - 166
eISSN - 1097-4628
pISSN - 0021-8995
DOI - 10.1002/app.22096
Subject(s) - syntactic foam , glass microsphere , materials science , composite material , ultimate tensile strength , scanning electron microscope , compression (physics) , tension (geology) , epoxy , cracking , tensile testing , microsphere , chemical engineering , engineering
Scanning Electron Microscopic (SEM) studies were carried out on the failure surface of syntactic foam material tested in a short beam three point bend test (SBT) by employing 21 × 15 × 3 mm 3 dimension bearing specimens. The syntactic foams were fabricated using glass microballoons in epoxy binder. The failure of the tensile, compression, and shear dominated regions were studied by SEM at different magnifications. The tensile region had characteristic features, such as partial debonding of the microballoons from the matrix and cracking of glass microballoons, apart from matrix cracking and some river pattern features. The compression side was characterized by crushing and collapsing of microballoons, resulting in accumulation of debris with no apparent river pattern for matrix‐rich regions. The midway positions of the SBT failed surface comprised of deformation bands in the matrix and occasional debonding of microballoons. The morphology recorded in the tensile and compression regions corroborated well with the results obtained on these foam samples in those specimens that were subjected to pure uniaxial tension and compression, respectively. © 2005 Wiley Periodicals, Inc. J Appl Polym Sci 98: 673–679, 2005