Premium
Activation of wood surface by corona treatment to improve adhesive bonding
Author(s) -
Sakata Isao,
Morita Mitsuhiro,
Tsuruta Natsuhi,
Morita Kenzo
Publication year - 1993
Publication title -
journal of applied polymer science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.575
H-Index - 166
eISSN - 1097-4628
pISSN - 0021-8995
DOI - 10.1002/app.1993.070490714
Subject(s) - wetting , adhesive , chemistry , contact angle , adsorption , aldehyde , dyeing , polymer chemistry , fraction (chemistry) , materials science , chemical engineering , composite material , organic chemistry , nuclear chemistry , layer (electronics) , catalysis , engineering
Oxidative activation of resinous wood surfaces by a corona treatment to improve adhesive bonding was studied. It was found that the wettability of the veneers, including hardwoods, softwoods, and tropical woods increased with an increase in the degree of treatment, and the gluability increased rapidly after the initial mild treatment. To elucidate the nature of any chemical change occurring on the wood surface, the dyeing examination of the wood and its components with Schiff's reagent was made, and the results showed a higher dyeing ability for corona‐treated samples compared to untreated ones, indicating that aldehyde groups increased by the corona treatment. The treatment affected the alcohol‐benzene extractives, and oxidized them to produce aldehyde groups. Especially, the neutral fraction in the extractives was significantly affected. On the other hand, negligible chemical effects of the treatment on the surface modification of the wood's main components were seen. Both the untreated and corona‐treated samples adsorbed basic dye to the same extent of coloration. Thus, no measurable carboxyl groups increased on the surface of the samples. It seems that an increase in the wettability of corona‐treated wood veneers resulted mainly from the oxidation of the high hydrophobic surface layer of neutral fraction substances in the extractives, and from the reduction in their hydrophobicity. © 1993 John Wiley & Sons, Inc.