Effect of polymerization initiator on early colour of poly(vinyl chloride)
Author(s) -
Rogestedt Mikael,
Jonsson Torbjörn,
Hjertberg Thomas
Publication year - 1993
Publication title -
journal of applied polymer science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.575
H-Index - 166
eISSN - 1097-4628
pISSN - 0021-8995
DOI - 10.1002/app.1993.070490612
Subject(s) - polyene , vinyl chloride , polymerization , chemistry , polymer chemistry , radical , heptane , suspension polymerization , polymer , acetone , degree of polymerization , organic chemistry , copolymer
The development of early colour and the dehydrochlorination rate were compared for poly(vinyl chloride) samples obtained by suspension polymerization using two different initiators, dicetylperoxydicarbonate and butylperoxyneodecanoate. The degree of discolouration was measured on pressed plates and expressed as yellowness index (YI), the polyene sequence distribution was monitored by UV/Vis‐spectroscopy, and the degradation rate was determined by measuring evolved HCI conductometrically. The PVC sample initiated by dicetylperoxydicarbonate exhibited more extensive early colour and a higher dehydrochlorination rate as compared to the sample obtained with butylperoxyneodecanoate as initiator. The UV/Vis‐spectra showed that the early colour originates from polyene sequences. After extraction of the PVC resins with heptane: acetone (85 : 15) the early colour turned out to be almost the same for the two samples. From 13 C‐NMR measurements it was found that the extract of the sample polymerized with dicetylperoxydicarbonate contains unreacted initiator. We suggest that the radicals formed when the remaining initiator decomposes initiate dehydrochlorination. Our results also indicate that radicals from dicetylperoxydicarbonate may cause long‐chain branches during polymerization. The radicals formed from butylperoxyneodecanoate, on the other hand, do not seem to react with the polymer molecules. © 1993 John Wiley & Sons, Inc.