Aromatic polyimides: Synthesis, characterization, and evaluation of electric strength
Author(s) -
Bjellheim Peter,
Helgee Bertil
Publication year - 1993
Publication title -
journal of applied polymer science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.575
H-Index - 166
eISSN - 1097-4628
pISSN - 0021-8995
DOI - 10.1002/app.1993.070480911
Subject(s) - electric field , gravimetric analysis , materials science , dibutyl phthalate , field strength , polymer , diamine , breakdown voltage , composite material , analytical chemistry (journal) , polymer chemistry , chemistry , magnetic field , organic chemistry , electrical engineering , voltage , engineering , physics , quantum mechanics
Aromatic polyimides have been synthesized via the formation of polyamic acids in solution. This solution was cast into films that were thermally imidized. The imidization process was monitored using FTIR. The degree of imidization was also determined with thermo‐gravimetric analysis. The electric breakdown field strength was tested under ac and dc conditions. Ac electric breakdown field strength measured in transformer oil was shown to follow a power‐law dependence on film thickness. This dependence was not affected by the molecular mass of the polymer but changed with the degree of imidization and the electron‐accepting properties of the diamine. High ac breakdown field values of polymides were obtained in dibutyl phthalate medium due to the suppression of partial discharges that occurs under these conditions. Measurements on films with thicknesses up to 60 μ showed no thickness dependence. No significant influence of the chemical structure on the break‐down field strength was observed under these conditions. Breakdown field measurements under dc conditions showed high values, which were in good agreement with the peak values of the ac measurements in dibutyl phthalate. This indicates similarities in the intrinsic ac and dc breakdown processes. © 1993 John Wiley & Sons, Inc.