Graft copolymerization of glass fiber and its application
Author(s) -
Hashimoto Koshiro,
Fujisawa Takao,
Kobayashi Masahiro,
Yosomiya Ryutoku
Publication year - 1982
Publication title -
journal of applied polymer science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.575
H-Index - 166
eISSN - 1097-4628
pISSN - 0021-8995
DOI - 10.1002/app.1982.070271201
Subject(s) - grafting , materials science , copolymer , benzoyl peroxide , flexural strength , styrene , composite material , flexural modulus , glass fiber , polymerization , polymer chemistry , polymer
Modified glass fibers, containing unsaturated hydrocarbon surface groups, were prepared by a hydrothermal treatment, with allylglycidylether in excess as reagent. Graft polymerization of the treated glass fiber with styrene and methylmethacrylate was carried out in sealed tubes, under nitrogen, using benzoyl peroxide (BPO) and cumene hydroperoxide (CHPO) as initiators. When BPO was used as the initiator, the grafting efficiency was extremely low, but the graft copolymerization behavior was similar to that of usual organic polymers. With CHPO, both grafting ratio and grafting efficiency were very high. Various properties of composite materials containing grafted glass cloth were studied. Flexural strength, flexural modulus, and interlaminar shear strength increased proportionally to the increase of the grafting ratio; the same values were decreased only in a small extent after the boiling test.