Binary and ternary blends of poly(vinyl chloride), hytrel, and a polyurethane
Author(s) -
Hourston D. J.,
Hughes I. D.
Publication year - 1981
Publication title -
journal of applied polymer science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.575
H-Index - 166
eISSN - 1097-4628
pISSN - 0021-8995
DOI - 10.1002/app.1981.070261025
Subject(s) - polyurethane , vinyl chloride , tetrahydrofuran , glass transition , materials science , ternary operation , polymer chemistry , polymer blend , polymer , phase (matter) , ether , polyvinyl chloride , copolymer , composite material , organic chemistry , chemistry , solvent , computer science , programming language
Binary blends of poly(vinyl chloride) and a poly(ether urethane) containing 20 and 40 weight percent, respectively, of poly(vinyl chloride) have been prepared by solution blending from tetrahydrofuran and their degree of mixing investigated using dynamic mechanical analysis. In the polyurethane, transitions were found at −19°C and −119°C. The former was attributed to the glass transition and the latter to a Schatzki type of motion of the polyether sequences. This latter transition occurred at a temperature which is higher than the literature value for the low temperature transition in poly(tetrahydrofuran), which is equivalent to the polyether sequence in the polyurethane. This discrepancy is attributed to the influence of neighboring hard segments present because of incomplete segmental phase separation of the polyurethane. For the blends only one very broad transition was observed, indicating that there was substantial mixing of these two polymers. Three ternary blends were prepared, also by solution blending, containing poly(vinyl chloride), Hytrel, and the polyurethane in the ratios 1:1:1, 1:2:1, and 2:1:1, respectively. In the first two blends there was clear evidence of phase separation. It was only in the 2:1:1 blend that an apparently significantly compatible material resulted.