Premium
Preparation and structures of the poly(vinyl chloride) porous membranes
Author(s) -
Hirose Sachio,
Shimizu Akira,
Nose Takuhei
Publication year - 1979
Publication title -
journal of applied polymer science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.575
H-Index - 166
eISSN - 1097-4628
pISSN - 0021-8995
DOI - 10.1002/app.1979.070231105
Subject(s) - membrane , vinyl chloride , casting , aqueous solution , membrane structure , materials science , polymer , chemical engineering , absorption of water , polymer chemistry , dimethylformamide , porosity , leaching (pedology) , chloride , chemistry , copolymer , composite material , organic chemistry , solvent , biochemistry , environmental science , soil science , metallurgy , engineering , soil water
Formation of membranes from a binary system, poly(vinyl chloride) and dimethylformamide, was studied. Phase separation during membrane formation was caused by absorption of aqueous vapor from the atmosphere. The membrane structure was closely related to the degree of phase separation. The membrane formation process was divided into three stages, i.e., an early stage, a transitional stage, and a late stage. By leaching the solution at the early stage, where the casting solution was still transparent, a membrane with a finger‐like structure was obtained. On the other hand, a network structure was obtained by leaching at the late stage which was dependent on the molecular weight and the concentration of poly(vinyl chloride). The membrane structure was predominantly controlled by the mobility of polymer molecules in the casting solution.