Synthesis and thermal properties of poly(urethane‐imide)
Author(s) -
Jiang Bibiao,
Hao Jianjun,
Wang Wenyun,
Jiang Luxia,
Cai Xinxian
Publication year - 2001
Publication title -
journal of applied polymer science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.575
H-Index - 166
eISSN - 1097-4628
pISSN - 0021-8995
DOI - 10.1002/app.1494
Subject(s) - imide , phthalic anhydride , thermogravimetric analysis , polymer chemistry , inherent viscosity , chemistry , solvent , intrinsic viscosity , polymer , materials science , organic chemistry , catalysis
The synthesis and thermal properties of thermoplastic poly(urethane‐imide) (PUI) resins were studied. Model reaction studies on the reactions of 4,4′‐diphenylcarbamatodiphenylmethane and 4,4′‐diisocyanatodiphenylmethane with phthalic anhydride were performed. We found that the reaction of anhydrides with urethane groups could take place under certain reaction conditions. According to the model reaction studies, N ‐2‐methyl‐pyrrolidone was employed as a solvent, and no catalyst was used in the polymerization. To restrain the side reaction of anhydrides with urethane groups, we adopted a two‐step chain‐extending procedure in a chain‐extending reaction. The inherent viscosity of PUI was 0.83–0.99 dL/g. The prepared polymers not only exhibited improved solubility in organic solvents but also formed flexible films. Thermogravimetric analysis showed that PUI exhibited a two‐step thermal weight‐loss pattern. The first step of the thermal degradation of PUI was attributed to the thermooxidizing cleavage of weak and labile linkage, such as urethane groups, isopropylidene, and methylene, except for imide rings. The polymer inherent viscosity decreased sharply during the first step of thermal degradation. © 2001 John Wiley & Sons, Inc. J Appl Polym Sci 81: 773–781, 2001