Elucidation of the miniemulsion stabilization mechanism and polymerization kinetics
Author(s) -
Anderson Christopher D.,
Sudol E. David,
ElAasser Mohamed S.
Publication year - 2003
Publication title -
journal of applied polymer science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.575
H-Index - 166
eISSN - 1097-4628
pISSN - 0021-8995
DOI - 10.1002/app.13105
Subject(s) - miniemulsion , polymerization , emulsion polymerization , pulmonary surfactant , nucleation , kinetics , particle size , particle (ecology) , polymer chemistry , materials science , chemical engineering , critical micelle concentration , styrene , chemistry , micelle , copolymer , organic chemistry , polymer , aqueous solution , physics , oceanography , quantum mechanics , engineering , geology
Styrene/hexadecane miniemulsions were polymerized at 50°C using a redox initiator. The miniemulsions and their corresponding latexes were characterized in terms of size, polymerization rate, and surface properties. The resulting data were analyzed to elucidate the miniemulsion stabilization and polymerization mechanisms. It was found that the free surfactant concentration exceeded the critical micelle concentration when large amounts of surfactant (60 m M sodium lauryl sulfate) were used, resulting in simultaneous micellar and droplet nucleation. Most surfactant was on the surface of the droplets (85%) or particles (95%). The fractional surface coverage was proportional to the surfactant concentration to the 0.55 power. Using a particle diameter equation, the number of particles was calculated to be proportional to the surfactant concentration to the 1.35 power. Through direct particle size measurements, a power of 1.38 was confirmed. The rate of polymerization was determined by reaction calorimetry to be proportional to the number of particles to the 0.59 power, in contrast to classical Smith–Ewart kinetics for conventional emulsions (1.0 power). The average number of radicals per particle was estimated from the rate and number data, and varied with the particle diameter to the 0.97 power. The observed kinetic dependencies were validated through an extension of Smith–Ewart theory. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 90: 3987–3993, 2003