Novel positive‐working aqueous‐base developable photosensitive polyimide precursors based on diazonaphthoquinone‐capped polyamic esters
Author(s) -
Hsu Steve LienChung,
Lee PoI,
King JinnShing,
Jeng JyhLong
Publication year - 2003
Publication title -
journal of applied polymer science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.575
H-Index - 166
eISSN - 1097-4628
pISSN - 0021-8995
DOI - 10.1002/app.12905
Subject(s) - aqueous solution , tetramethylammonium hydroxide , polymer chemistry , polyimide , materials science , chemistry , organic chemistry , composite material , nanotechnology , layer (electronics)
Novel positive‐working aqueous‐base developable photosensitive polyimide (PSPI) precursors based on partially diazonaphthoquinone (DNQ)‐capped polyamic esters bearing phenolic hydroxyl groups and a DNQ photosensitive compound (PIC‐3) were developed. The partially DNQ capped polyamic esters were prepared from an esterification reaction of 1,2‐naphthoquinone diazide‐5‐sulfonyl chloride with the polyamic esters. The partially DNQ capped polyamic esters decreased the dark film loss effectively in the aqueous‐base developer and were able to make thicker film resists compared to the uncapped polyamic esters. The 25 mol % DNQ‐capped BisAPAF–PMDA polyamic ester and BisAPAF–ODPA polyamic ester containing 25 wt % PIC‐3 photosensitive compound showed a sensitivity of 176 and 185 mJ/cm 2 , and a contrast of 1.68 and 1.02, respectively, in a 3‐μm film with 1.25 wt % tetramethylammonium hydroxide developer. A pattern with a resolution of 5 μm was obtained from both PSPI precursor compositions. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 90: 2293–2300, 2003