Study of rheological property of nylon‐1212 with Haake Rheometer
Author(s) -
Zhang Chenggui,
Liu Minying,
Zhao Qingxiang,
Wang Yudong,
Liu Songtao
Publication year - 2003
Publication title -
journal of applied polymer science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.575
H-Index - 166
eISSN - 1097-4628
pISSN - 0021-8995
DOI - 10.1002/app.11929
Subject(s) - creep , materials science , rheometer , rheology , viscoelasticity , activation energy , nylon 6 , composite material , shear rate , shear stress , viscosity , shear (geology) , polymer , chemistry , organic chemistry
Abstract Rheological properties of nylon‐1212 have been studied by means of Haake Rheometer. The effect of shear rate and temperature on the apparent vicosity of nylon‐1212 was discussed. A correlation of non‐Newtonian index with the temperature was obtained. The results showed that the apparent viscosity decreases with the increase of the temperature. With increasing shear rate, shear thinning of nylon‐1212 was observed clearly. From the relation of the temperature dependence of the polymer, we obtained the viscous flow activation energy. We conclude that the apparent viscosity is sensitive to temperature at lower shear stress because of higher viscous flow activation energy, and the temperature affect on the apparent viscosity becomes weaker at higher shear stress because of lower viscous flow activation energy. We have investigated the creep and elastic recovery of nylon‐1212. A creep test was carried out to define the linear viscoelastic range as 1.0 and 5.0 Pa for 195 and 190°C nylon‐1212 melts, respectively. A time‐dependent response was found for the creep and recovery phases at a lower applied shear stress. However, at higher shear stress, the creep and recovery phases were time‐independent. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 89: 379–385, 2003