Characterization of air plasma‐treated polymer surfaces by ESCA and contact angle measurements for optimization of surface stability and cell growth
Author(s) -
Johansson BoLennart,
Larsson Anders,
Ocklind Anette,
Öhrlund Åke
Publication year - 2002
Publication title -
journal of applied polymer science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.575
H-Index - 166
eISSN - 1097-4628
pISSN - 0021-8995
DOI - 10.1002/app.11209
Subject(s) - contact angle , materials science , polystyrene , polymer , chemical engineering , polymer chemistry , x ray photoelectron spectroscopy , copolymer , wetting , composite material , engineering
Abstract A radiofrequency air plasma has been used to incorporate new functionalities at the surface of cycloolefin polymers (Zeonex® and Topas®), polymethyl methacrylate (PMMA), styrene–acrylonitrile copolymer (SAN), and polystyrene (PS). The main goals with the plasma treatment of the different plastics were to hydrophilize the surfaces and to provide good cell culture properties. Surfaces treated at high RF power/gas flow ratios (50 to 100 W/sccm) became highly hydrophilic (water contact angles of about 5 degrees) and stable towards washing in 70% (v/v) ethanol. Those treated at lower power/gas flow ratios (3 to 10 W/sccm) were less hydrophilic and not wash‐stable. Cell growth properties of HeLa cervix carcinoma cells as good as on commercial tissue‐culture polystyrene could be obtained for Zeonex, SAN, and PS, treated at relatively low RF power/gas flow ratios. However, no untreated plastics were suitable for culturing these cells. XPS spectra features show that ester, ether/alcohol, and ester/carboxyl groups are formed during the plasma treatments of the different plastics. Measurable amounts of carboxylic acid carbon after plasma treatment were only observed for PS and Topas. Furthermore, at high RF power/gas flow ratios fluorine, aluminium and silicon were incorporated in all investigated plastics surfaces due to ablation–deposition processes in the reaction chamber. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 86: 2618–2625, 2002