Preparation and characterization of organic–inorganic hybrids and coating films from 3‐methacryloxypropylpolysilsesquioxane
Author(s) -
Gunji Takahiro,
Makabe Yoshie,
Takamura Norihiro,
Abe Yoshimoto
Publication year - 2001
Publication title -
applied organometallic chemistry
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.53
H-Index - 71
eISSN - 1099-0739
pISSN - 0268-2605
DOI - 10.1002/aoc.213
Subject(s) - coating , ethylene , chemistry , aluminium , adhesive , dip coating , refractive index , hydrolysis , polymer chemistry , chemical engineering , condensation polymer , composite material , nuclear chemistry , catalysis , materials science , organic chemistry , layer (electronics) , optoelectronics , engineering
3‐Methacryloxypropylpolysilsesquioxane (MA‐PS) was prepared by acid‐ or base‐catalyzed hydrolytic polycondensation of 3‐methacryloxypropyltrimethoxysilane (MAS). MA‐PS coating film was prepared by dip‐coating on organic, metal and inorganic substrates, including poly(ethylene terephthalate), aluminum, stainless steel, and glass. The coating films on poly(ethylene terephthalate) and glass showed high adhesive strength. The hardness of coating films increased with increasing heat treatment temperature, whereas they decreased with increasing H 2 O/MAS molar ratio. The refractive index of coating films increased with increasing heat treatment temperature. In addition, flat and transparent free‐standing films (0.24–0.27 mm thickness) were prepared from MA‐PS that were crack‐free after heat treatment at 1000 °C. Copyright © 2001 John Wiley & Sons, Ltd.